FEATURES
OTP Gold is constructed out of the finest grade of water-resistant plywood to withstand the continuous frequent shifts of dry & wet conditions. Graded core veneers of the highest quality are used to manufacture them as they are free of defects.
- CONTROLLED MOISTURE CONTENT
- BORER PROOF & TERMITE RESISTANT
- GLUED CORE PROTECTION
- SMOOTH SURFACE
- GURJAN FACE VENEER
- GURJAN CORE VENEER
- SUPERIOR FINISH
- WEATHER STABLE
PRODUCT SPECIFICATION
| TEST | ISI SPECIFIED VALUE | RESULT OBTAINED |
|---|---|---|
|
Moisture |
5% – 15% |
8% |
|
Glue Shear Strength (after 72 hrs. Boiling) |
Min. Ind. 1100 N Min. Avg 1350 N |
1350 N 1500 N |
|
Adhesion to plywood |
Min. Pass Standard |
Excellent |
|
Glue Shear Strength (after 72 hrs. Boiling) |
Min. Ind. 800 N Min. Avg 1000 N |
1350 N 1250 N |
|
Static Bending Strength
Modulus of Rupture – Along the grain – Across the grain |
50 N /sq.mm 30 N /sq.mm |
65 N /sq.mm 40 N /sq.mm |
|
Modulus of Elasticity – Along the grain – Across the grain |
7500 N / sq.mm 4000 N / sq.mm |
8305 N / sq.mm 4170 N / sq.mm |
|
Tensile Strength – Along the grain – Across the grain – Sum of Tensile strength |
42 N / sq.mm 25 N / sq.mm 84.5 N / sq.mm |
55 N / sq.mm 39 N / sq.mm 94 N / sq.mm |
|
Wet Bending Strength A. Along the face grain a) Modulus of Elasticity, N/mm2 b) Modulus of Rupture, N/mm2 B. Across the face grain a) Modulus of Elasticity, N/mm2 b) Modulus of Rupture, N/mm2 |
Avg: 3750 N/mm2 Min Ind: 3400 N/mm2 Avg: 25 N/mm2 Min Ind: 22 N/mm2 Avg: 2000 N/mm2 Min Ind: 1800 N/mm2Avg: 15 N/mm2 Min Ind: 13 N/mm2 |
4650 N/mm2 4100 N/mm2 30 N/mm2 26 N/mm2 3050 N/mm2 2500 N/mm225 N/mm2 20 N/mm2 |
OTP Gold is constructed out of the finest grade of water-resistant plywood to withstand the continuous frequent shifts of dry & wet conditions. Graded core veneers of the highest quality are used to manufacture them as they are free of defects.
- CONTROLLED MOISTURE CONTENT
- BORER PROOF & TERMITE RESISTANT
- GLUED CORE PROTECTION
- SMOOTH SURFACE
- GURJAN FACE VENEER
- GURJAN CORE VENEER
- SUPERIOR FINISH
- WEATHER STABLE
| TEST | ISI SPECIFIED VALUE | RESULT OBTAINED |
|---|---|---|
|
Moisture |
5% – 15% |
8% |
|
Glue Shear Strength (after 72 hrs. Boiling) |
Min. Ind. 1100 N Min. Avg 1350 N |
1350 N 1500 N |
|
Adhesion to plywood |
Min. Pass Standard |
Excellent |
|
Glue Shear Strength (after 72 hrs. Boiling) |
Min. Ind. 800 N Min. Avg 1000 N |
1350 N 1250 N |
|
Static Bending Strength
Modulus of Rupture – Along the grain – Across the grain |
50 N /sq.mm 30 N /sq.mm |
65 N /sq.mm 40 N /sq.mm |
|
Modulus of Elasticity – Along the grain – Across the grain |
7500 N / sq.mm 4000 N / sq.mm |
8305 N / sq.mm 4170 N / sq.mm |
|
Tensile Strength – Along the grain – Across the grain – Sum of Tensile strength |
42 N / sq.mm 25 N / sq.mm 84.5 N / sq.mm |
55 N / sq.mm 39 N / sq.mm 94 N / sq.mm |
|
Wet Bending Strength A. Along the face grain a) Modulus of Elasticity, N/mm2 b) Modulus of Rupture, N/mm2 B. Across the face grain a) Modulus of Elasticity, N/mm2 b) Modulus of Rupture, N/mm2 |
Avg: 3750 N/mm2 Min Ind: 3400 N/mm2 Avg: 25 N/mm2 Min Ind: 22 N/mm2 Avg: 2000 N/mm2 Min Ind: 1800 N/mm2Avg: 15 N/mm2 Min Ind: 13 N/mm2 |
4650 N/mm2 4100 N/mm2 30 N/mm2 26 N/mm2 3050 N/mm2 2500 N/mm225 N/mm2 20 N/mm2 |